Título: Laüe back-reflection method for crystallographic orientation of a martensitic Cu-Zn-Al single crystal of the monoclinic system
Autor(es): Zambrano, Uíslei Carlos
Blanco, Matildes
Barelli, Nilso
Benedetti, Assis Vicente
Fernández, Javier
Abstract: A martensitic single crystal Cu-23.95Zn-3.62(wt.%)Al alloy was obtained melting pure Cu, Zn and Al using Bridgman's method. The martensitic phase (monoclinic) can present up to 24 variants, and orienting the surface according to a certain plane is a very hard task. The single crystal was submitted to 8 tons of tension (stress) along the longitudinal direction to reduce the number of variants and facilitate the surface orientation according to the desired plane. This single crystal was oriented using the Laüe back-reflection method to give surfaces with the following oriented crystallographic planes: (010), (120) and (130). It was observed that the tension stress was applied along the [010] direction.
Palavras-chave: Eletroquímica
Cobre
Cristalografia
Editor: Química Nova
Citação: ZAMBRANO, Uíslei Carlos et al . Laüe back-reflection method for crystallographic orientation of a martensitic Cu-Zn-Al single crystal of the monoclinic system. Quím. Nova, São Paulo, v. 31, n. 1, 2008 . Disponível em <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0100-40422008000100027&lng=pt&nrm=iso>. acessos em 30 ago. 2011. http://dx.doi.org/10.1590/S0100-40422008000100027.
Tipo de Acesso: Acesso Aberto
Identificador DOI: http://dx.doi.org/10.1590/S0100-40422008000100027
URI: https://repositorio.ufms.br/handle/123456789/470
Data do documento: 2008
Aparece nas coleções:CPCS - Artigos publicados em periódicos

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Laue back-reflection.pdf3,62 MBAdobe PDFThumbnail
Visualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.